镁铬砖的产品介绍
镁铬砖一般是由烧结镁砂和耐火级铬矿为原料生产的，耐火晶粒间为硅酸盐结合，国内所说的镁铬砖，一般是指烧成的普通镁铬砖，简称镁铬砖。
镁铬砖的耐火度大于2000℃，荷重软化温度一般在1550℃以上，高温体积稳定性好，耐急冷急热性比镁砖强。
镁铬砖的规格参数
再结合镁铬砖
| Item | Behaviors | ||||
| Magnesia Chrome Bricks | |||||
| TY-AMC-40 | TY-AMC-20 | TY-AMC-12 | TY-AMC-8 | ||
| Chemical Composition 化学指标 | MgO ％ | 35 | 60 | 70 | 70 |
| SiO2 ％ | 1.0 | 1.0 | 2.0 | 2.0 | |
| Cr2O3 ％ | 40 | 20 | 12 | 8 | |
| 显气孔率Apparent Porosity ％ | 16 | 16 | 18 | 18 | |
| 耐压强度Cold Crushing Strength Mpa | 40 | 40 | 40 | 40 | |
| 荷重软化温度0.2Mpa Refractoriness Under Load T0.6 | 1700 | 1700 | 1650 | 1650 | |
| 体积密度Bulk Density g/cm3 | 3.3 | 3.15 | 3.05 | 3.0 | |
直接结合镁铬砖
| Item | Behaviors | ||||
| Magnesia Chrome Bricks | |||||
| TY-DMC-20 | TY-DMC-18 | TY-DMC-12 | TY-DMC-8 | ||
| Chemical Composition 化学指标 | MgO ％ | 55 | 60 | 65 | 80 |
| SiO2 ％ | 2.5 | 2.4 | 1.5 | 1.5 | |
| Cr2O3 ％ | 20 | 18 | 18 | 18 | |
| 显气孔率Apparent Porosity ％ | 18 | 18 | 18 | 18 | |
| 耐压强度Cold Crushing Strength Mpa | 40 | 40 | 40 | 40 | |
| 荷重软化温度0.2Mpa Refractoriness Under Load T0.6 | 1700 | 1700 | 1680 | 1650 | |
| 体积密度Bulk Density g/cm3 | 3.15 | 3.1 | 2.98 | 2.95 | |