Category | Trade- | Equivalent to China Standard | Characteristics & application | Equivalent to AWS |
Hard-surfacing 硬 面 堆 焊 | D 667 | EDZCr-B-15 | HRc≥48. Resistance to wear, gas corrosion and oxidation. Hardfacing of blast furnace hopper and cracker part. |
|
D 802 | EDCoCr-A-03 | HRc38-47. Resistance to heat, wear and corrosion. Hardfacing of high temperature part such as the edge of thermo-cutter. | ECoCr-A | |
D 812 | EDCoCr-B-03 | HRc45-50. Resistance to heat, wear and corrosion. Hardfacing of high temperature part such as internal-combustion engine valve. | ECoCr-B | |
D 822 |
| HRc≥53. Resistance to Wear and heat, bad shock resistance. Hardfacing of rotating blade wheel of boiler. |
| |
D 832 | EDCoCr-C-03 | HRc≥50. Wear and heat resistance. Hardfacing of high temperature part such as hot-rolling guided way. | ECoCr-C | |
D 842 | EDCoCr-D-03 | HRc28-38. Corrosion and thermo-fatigue resistance, work harding. Hardfacing of hot forging die. |
|
D802钴铬钨合金焊芯的钴基堆焊焊条，采用直流反接，堆焊金属在650℃工作仍能保持良好的耐磨性和耐腐蚀性，用于要求在650℃左右工作仍能保持良好的耐磨性和耐腐蚀性的场合，或承受冲击和冷热交错的部位，如堆焊高温高压阀门及热剪切刀刃等。
熔敷金属化学成分/%
C-0.70～1.40 Si≤2.0 Mn≤2.0 Cr-25.0～32.0 Fe≤4.0 W-3.0～6.0 其他≤4.0 Co-余量
堆焊层硬度HRC≥40
D812钴铬钨合金焊芯的钴基堆焊焊条，采用直流反接，堆焊金属在650℃工作仍能保持良好的耐磨性和耐蚀性，用于高温高压阀门、高压泵的轴套筒和内衬套筒以及化钎设备的斩刀刃口等
熔敷金属化学成分/%
C-1.00～1.70 Si≤2.00 Mn≤2.00 Cr-25.0～32.0 Fe≤5.0 W-7.0～10.0 其他≤4.0 Co-余量
堆焊层硬度HRC≥44
D822钴基堆焊焊条 D822是高碳钴铬钨合金焊芯的钴基堆焊焊条，采用直流反接，渣覆盖性好，成形美观，具有优良的耐磨、耐热和耐腐蚀性，在650℃高温也能保持这些特性。用于牙轮钻头轴承、锅炉的旋转叶轮、粉碎机刃口.螺旋送料机等磨损部件的堆焊
焊缝金属化学成分（％）
C--1.75～3.0 Cr--25.0～33.0 W--11.0～19.0 Mn--≤2.0 Si--≤2.0 Fe--≤5.0 Co--余量 其他总量≤4.0
堆焊层硬度HRC≥53
参考电流：
规格φ（mm） 4.0 5.0 6.0
电流（A） 120～160 140～190 150～210
D842钴基堆焊焊条 说明：钴基4号低碳钴铬钨合金焊芯的堆焊焊条，采用直流反接，堆焊金属在800℃仍能保持良好的看热疲劳性和耐蚀性。
用途：用于高温条件下承受冲击和冷热交错的工件堆焊，如热锻模，阀门密封面等，具有良好的性能。
熔敷金属化学成分/%
C Si Mn Cr Fe W 其他 Co
0.20~0.50 ≤2.00 ≤2.00 23.0~32.0 ≤5.00 ≤9.50 ≤7.00 余量
堆焊层硬度HRC28~35