产品 · 参数
| 高铬铸铁标准规范 | ||||||||||
| 参考标准 （ISO 21988-2005） | 化学成分（W%） | 对应国际标准 Eqv. Standards | ||||||||
| C | Si | Mn | Ni | Cr | Mo | Cu | P | S | ||
| ISO 21988/JN/ HBW555XCr13 | 1.8-3.6 | ≤1.0 | 0.5-1.5 | ≤2.0 | 11.0-14.0 | ≤3.0 | ≤1.2 | ≤0.08 | ≤0.08 | EN-GJN-HV600(XCr11) ASTM A532 12% Cr |
| ISO 21988/JN/ HBW555XCr16 | 1.8-3.6 | ≤1.0 | 0.5-1.5 | ≤2.0 | 14.0-18.0 | ≤3.0 | ≤1.2 | ≤0.08 | ≤0.08 | EN-GJN-HV600(XCr14) ASTM A532 15% Cr-Mo AS 2027 CrMo 15 3 G-X 300 CrMoNi 15 2 1 |
| ISO 21988/JN/ HBW555XCr21 | 1.8-3.6 | ≤1.0 | 0.5-1.5 | ≤2.0 | 18.0-23.00 | ≤3.0 | ≤1.2 | ≤0.08 | ≤0.08 | EN-GJN-HV600(XCr18) ASTM A532 20% Cr-Mo AS 2027 CrMo 20 1 G-X 260 CrMoNi 20 2 1 |
| ISO 21988/JN/ HBW555XCr27 | 1.8-3.6 | ≤1.0 | 0.5-2.0 | ≤2.0 | 23.0-30.0 | ≤3.0 | ≤1.2 | ≤0.08 | ≤0.08 | EN-GJN-HV600(XCr23) ASTM A532 25% Cr-Mo AS 2027 Cr27 LC & Cr27 HC G-X 260 Cr27 |
| ISO 21988/JN/ HBW600XCr35 | 3.0-5.5 | ≤1.0 | 1.0-3.0 | ≤1.0 | 30.0-40.0 | ≤1.5 | ≤1.2 | ≤0.06 | ≤0.06 | AS 2027 Cr35 |
| ISO 21988/JN/ HBW600XCr20Mo2Cu | 2.6-2.9 | ≤1.0 | ≤1.0 | ≤1.0 | 18.0-21.0 | 1.4-2.0 | 0.8-1.2 | ≤0.06 | ≤0.06 | AS 2027 CrMoCu 20 2 1 |
性能 · 特点
产品性能
材质：高铬铸铁，铬-钼-镍多合金钢
尺寸：客户定制
性能：高锰钢：水韧性处理，HB≤229，金相组织（A + C），冲击值（≥80J/ cm2）；
合金钢：油淬处理，HRC40-50，金相组织（M + C），冲击值（≥40J/ cm2）
初始硬度：350 HBW
使用后硬度：540 HBW
冲击韧性：≥120-150J /cm²
最小起订量：1吨
产能：25000吨/年
产品特点
应用领域：双进双出磨煤机
特色：优异的耐磨性，长寿命，强韧性